Effect of CrF 3 on the corrosion behaviour of Hastelloy-N and 316L stainless steel alloys in FLiNaK molten salt

Abstract The effect of CrF 3 on the corrosion behaviour of Hastelloy-N and 316L austenitic stainless steel alloys in FLiNaK at 700 °C was investigated using synchrotron radiation and other characterisation techniques. The results showed that CrF 3 considerably accelerated the corrosion of both tested alloys by promoting the dissolution of Cr, Fe, and Mn from alloy matrices into molten salt. The 316L stainless steel alloys mainly exhibited intergranular corrosion, whereas the Hastelloy-N alloys tended to exhibit intergranular and pitting corrosion. After corrosion, the lattice parameter of both alloys decreased and Cr 1.07 Fe 18.93 was formed on the surface of the 316L stainless steel alloys.