Synthesis of Nanostructured/Macroscopic Low-Density Copper Foams Based on Metal-Coated Polymer Core–Shell Particles

A robust, millimeter-sized low-density Cu foam with ∼90% (v/v) porosity, ∼30 nm thick walls, and ∼1 μm diameter spherical pores is prepared by the slip-casting of metal-coated polymer core–shell particles followed by a thermal removal of the polymer. In this paper, we report our key findings that enable the development of the low-density Cu foams. First, we need to synthesize polystyrene (PS) particles coated with a very thin Cu layer (in the range of tens of nanometers). A simple reduction in the amount of Cu deposited onto the PS was not sufficient to form such a low-density Cu foams due to issues related to foam collapse and densification upon the subsequent polymer removal step. Precise control over the morphology of the Cu coating on the particles is essential for the synthesis of a lower density of foams. Second, improving the dispersion of PS–Cu particles in a suspension used for the casting as well as careful optimization of a baking condition minimize the formation of irregular large voids, leadi...