Heavy-ion irradiation and post-irradiation annealing effects in explosion-welded CuCrZr/316LN joints for ITER application

Abstract Bimetallic plates of CuCrZr/316LN are important heat sink components in the ITER first wall. Their in-reactor performance was investigated with 6.4 MeV Fe3+ ion irradiation (500 °C/10.5 dpa), as an analogue for neutron damage. Detailed characterizations showed that the CuCrZr/316LN joints have maintained good structural integrity after irradiation. The as-irradiated interface consisted of a nanocrystalline interlayer, typically of