Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Abstract Specimens of the glassy system: (70 −  x )TeO 2  + 15B 2 O 3  + 15P 2 O 5  +  x Li 2 O, where x  = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO 2 by Li 2 O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200–800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E opt , and width tails, Δ E , are determined. It is observed that E opt is decreased and Δ E increased with the increase of Li 2 O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.