Morphology and the isoelectric point of nanosized aqueous ceria sols

Abstract Ceria sols were synthesized by a forced hydrolysis method using cerium sulphate or cerium nitrate as precursors. High-resolution TEM was used to determine the microstructure and particle size of CeO 2 . A polycrystalline structure of ceria sols with crystallite sizes of 4.4 and 8.6 nm was obtained. The particles had a well-defined polyhedral shape. Direct bandgaps for ceria nanoparticles were 2.80 and 3.31 eV, respectively. The isoelectric point, pH iep , of ceria sols in KNO 3 solutions was investigated. The isoelectric point of ceria was found to be pH iep  = 7.6 ± 0.2. The obtained results indicate that the isoelectric point in the presence of SO 4 2− ions shifts to lower pH value. The particle size of ceria increases with pH, reaching the maximum value at pH iep as the result of agglomeration .