Comparative mechanical and microstructural properties of high calcium fly ash one-part geopolymers activated with Na2SiO3-anhydrous and NaAlO2

Abstract This paper investigates the effect of varying solid alkali activators on the fresh and hardened properties and microstructural changes of one-part geopolymers (OPGs). Single and binary solid alkali activators were used to activate high calcium fly ash. The alkali activators were either solely sodium metasilicate (Na2SiO3) or a combination of sodium aluminate (NaAlO2) and sodium metasilicate (Na2SiO3). The OPG activated with anhydrous Na2SiO3 achieved an excellent 28-day compressive strength of 83.6 MPa while OPG activated with NaAlO2 and Na2SiO3 attained a compressive strength of 45.1 MPa. The Na2SiO3-activated OPG demonstrated better fluidity than the OPG activated with NaAlO2 and Na2SiO3 due to the thixotropic behaviour caused by the NaAlO2. The Na2SiO3-activated OPG consisted of sodium-calcium aluminium silicate hydrate ((N,C)-A-S-H) gel phase, while the OPG activated with NaAlO2 and Na2SiO3 comprised of the coexistence of sodium aluminium silicate hydrate (N-A-S-H) and calcium aluminium silicate hydrate (C-A-S-H) gel phases. Regardless of the distinctive properties, the OPGs are adequate for building materials applications.