Radioactive waste conditioning: the choice of the cement matrix versus irradiation

The aim of this study is to compare the behavior of Portland and Ciment Fondu® cement under irradiation taking into account both real cement pastes and synthetic hydrates. First, γ-irradiations were performed using a 60 Co source (dose rate: 0.17-0.25 Gy.s-1, dose: up to 500×10 3 Gy). Thermogravimetric analysis measurements were performed in order to determine the amount and the type of water involved. H2 gas production was measured by gas chromatography. Regardless of the water to cement ratio (W/C) chosen (0.2, 0.4 and 0.6), it is shown that Ciment Fondu® pastes produce less H2 under irradiation. Moreover, the H2 production of portlandite and gibbsite, constituent hydrates of Portland and Ciment Fondu® cements respectively, shows that the amount of gas produced depends on the hydrate nature. Secondly, portlandite and gibbsite were electron-irradiated up to 300 MGy and 3 GGy using the LSI SIRIUS accelerator platform. X-Ray Diffraction analyses were performed before and after irradiation in order to investigate structural damage. Only limited structural disorder was observed, which confirms the good stability of both hydrates under present irradiation conditions.