COMPARISON OF SODIUM AND POTASSIUM CARBONATES AS LITHIUM ZIRCONATE MODIFIERS FOR HIGH-TEMPERATURE CARBON DIOXIDE CAPTURE FROM BIOMASS-DERIVED SYNTHESIS GAS

The process of gasifi cation converts biomass into synthesis gas (syngas), which can be used to produce biofuels. Solid-phase sorbents were investigated for the removal of CO2 from a N2/CO2 gas stream using a CO2 concentration similar to that found in a biomass gasifi cation process. During the gasifying process, large amounts of carbon dioxide (CO2) are created along with the syngas. The produced CO2 must be removed before the syngas can be used for fuel synthesis and to avoid the possible formation of unwanted byproducts. A thermogravimetric analyzer was used to test the CO2 absorption rates of sorbents composed of lithium zirconate (Li2ZrO3), as well as mixtures of Li2ZrO3 with potassium carbonate (K2CO3) and sodium carbonate (Na2CO3). The experimental results show that Li2ZrO3 has a low absorption rate, but sorbents containing combinations of Li2ZrO3 and the K2CO3 and Na2CO3 additives have high uptake rates. Using different proportions of K2CO3 and Na2CO3 produces varying uptake rates, so an optimization experiment was performed to obtain an improved sorbent. The CO2 absorption and regeneration stability of the solid-phase sorbents were also examined. A sorbent composed of Li2ZrO3 and 12.1 weight % Na2CO3 was shown to be stable, based on the consistent CO2 uptake rates. Sorbents prepared with Li2ZrO3, 17.6 weight % K2CO3 and 18.1 more » weight % Na2CO3 showed instability during regeneration cycles in air at 800 °C. Sorbent stability improved during regeneration cycles at 700 °C. Further testing of the Li2ZrO3 sorbent under actual syngas conditions, including higher pressure and composition, should be done. Once the optimum sorbent has been found, a suitable support will be needed to use the sorbent in an actual reactor. « less