Transition Pathway between Gyroid and Cylindrical Morphology in Linear Triblock Terpolymer Thin Films

A new transition between alternating gyroid (GA) structure and cylindrical morphology was observed in thin films for a poly(isoprene-block-styrene-block-(2-vinylpyridine)) (ISP) triblock terpolymer (I/S/P volume fraction = 0.20:0.66:0.14) exhibiting in bulk a Q214 (space group I4132) morphology. Thin films were organized using solvent vapor annealing (SVA) and characterized by atomic force microscopy, transmission electron microscopy, and grazing-incidence small-angle X-ray scattering, coupled with several selective revealing methods adapted to the ISP system. After a short SVA time, the bulk morphology was reproduced with the (011) plane parallel to the surface. With a longer annealing time, a P2mm structure with cylindrical polyisoprene (PI) and poly(2-vinylpyridine) (P2VP) domains was obtained. Evidence of domains in transition between gyroid and cylinders was found, suggesting an epitaxial relationship between these two structures. In contrast to the well-known double gyroid (GD) to hexagonal (HEX) tr...