Corrosion Rates of Zircaloy-4 by Hydrogen Measurement under High pH, Low Oxygen and Low Temperature Conditions
2012
Corrosion tests of Zircaloy-4 were performed in a dilute NaOH solution (pH =12.5) at 303 K for 90 days using the gas flow system (oxygen; where x represents the Zircaloy-4 hydrogen absorption ratio. The initial hydrogen content in the Zircaloy-4 specimen was controlled to be below 10 ppm. The corrosion rate decreased with time (90-day values: 2.46×10 -3 and 2.37×10 -3 μm/y for the gas flow method and 6.72×10 -2 μm/y for the batch test). The Zircaloy-4 hydrogen absorption ratio during corrosion was over 90%. The large amount of hydrogen absorbed in Zircaloy-4 will play an important role in the long-term safety for the disposal of irradiated Zircaloy materials.