Synthesis of Thermally Stable χ-Alumina by Thermal Decomposition of Aluminum Isopropoxide in Toluene

Thermal decomposition of aluminum isopropoxide in toluene at 315°C resulted in χ-alumina that had high thermal stability, whereas the reaction at lower temperatures resulted in formation of an amorphous product. The χ-alumina thus obtained directly transformed to α-alumina at ∼1150°C, bypassing the other transition alumina phases, whereas the amorphous product transformed to γ-alumina and then to θ-alumina before final transformation to α-alumina. When the χ-alumina, solvothermally synthesized at 315°C, was recovered by the removal of the solvent at the reaction temperature, thermal stability of the product was improved further. This procedure is convenient because it avoids bothersome work-up processes that yield large-surface-area and large-pore-volume alumina.