Evaluation of Ca-doped BaZrO3 as the crucible refractory for melting TiAl alloys
2018
Abstract In this study, a new Ca-doped BaZrO 3 refractory was designed by using thermodynamics approaches and tested for its applicability for vacuum induction melting (VIM) of TiAl alloys. The influence of CaO on the BaZrO 3 phase constitution and microstructure, as well as the key features of the TiAl melt interaction with the Ca-doped BaZrO 3 crucibles were investigated by X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). Results revealed that the Ca-doped BaZrO 3 refractory consisted of Ba 1-x Ca x ZrO 3 and CaO phases. An obvious interaction occurred during the melting of the TiAl alloy in the Ca-doped BaZrO 3 crucible along with the generation of BaAl 2 O 4 as a reaction product, with formation of a reaction layer up to 5 µm thick. Dissolution of Ca-doped BaZrO 3 refractory in the TiAl melt was the main reason for the alloy-crucible reaction. Moreover, the Ca-doped BaZrO 3 crucible was found to substantially reduce the contamination of the TiAl alloy, with lower oxygen concentration as compared with other conventional oxide crucibles. Overall results confirmed that vacuum induction melting using the Ca-doped BaZrO 3 refractory can be considered as an appropriate method for the fabrication of TiAl alloys.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
20
References
9
Citations
NaN
KQI