Ultrafast preparation of branched poly(methyl Acrylate) through single electron transfer living radical polymerization at room temperature

Ultrafast preparation of branched poly(methyl acrylate) (BPMA) with high-molecular weight through single electron transfer living radical polymerization (SET-LRP) of inimer at 25°C has been attempted, atom transfer radical polymerization (ATRP) at 60°C was also carried out for comparison. Gas chromatography, proton nuclear magnetic resonance, and triple detection size exclusion chromatography were used to analyze these polymerizations. As expected, SET-LRP system showed much faster polymerization rate than ATRP system, the calculated apparent propagation rate constants (kpapp) are 3.69 × 10−2 min−1 and 6.23 × 10−3 min−1 for SET-LRP and ATRP system, respectively. BPMA with high-molecular weight (Mw.MALLS = 86,400 g mol−1) compared with that in ATRP (Mw.MALLS = 61,400 g mol−1) has been prepared. POLYM. ENG. SCI., 54:1579–1584, 2014. © 2013 Society of Plastics Engineers