Tailoring mechanical behavior of a fine-grained metastable austenitic stainless steel by pre-straining
2019
Abstract A fine-grained AISI 304 austenitic stainless steel (ASS) was fabricated by cryogenic-rolling and cycle annealing. The fine-grained ASS was pre-strained to various strains of 0–0.16, and the corresponding microstructures, kinetics of strain-induced α ′-martensite (SIM α ′ ) and work-hardening behavior were investigated based on quantitative characterization, interrupted-tensile tests and physical metallurgy. We find that the yield strength of the ASS can be enhanced by combining grain-refining with pre-straining due to the strengthening effect of grain-refinement, dislocations, shear bands and SIM α ′ . The formation rate of shear band increases with increasing pre-strain ( e p ) and the probability for an intersection of shear band to form a SIM α ′ embryo is insensitive to the pre-strain, and as a result, the kinetics of SIM α ′ is accelerated by pre-straining. The fine-grained ASS with e p ≈ 0–0.16 display a three-stage work-hardening behavior, and the corresponding Stage I, II and III are completed in advance mainly due to their faster kinetics of SIM α ′ and severer dynamic recovery caused by pre-straining. The work-hardening rate ( Θ ) of pre-strained fine-grained ASS decreases faster than that of non-pre-strained counterpart at Stage I, accompanying with dislocations-dominated hardening. The Θ ascend with increasing strain to a peak value at Stage II and then decline continuously to necking at Stage III, following as SIM α ′ -governed hardening, which can be tailored by grain-refining and pre-straining. Our studies provide the direct experimental evidence for the pre-straining to trim the kinetics of SIM α ′ in a fine-grained ASS. These observations help to deepen understanding of the effect of pre-strain on the mechanical behavior of other fine-grained strengthening ASS and transformation-induced-plasticity (TRIP) assisted alloy.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
36
References
11
Citations
NaN
KQI