Ultrafine-grained (UFG) Mg-3Al-1Zn (AZ31) alloys with gain sizes ranging from 0.46 to 3.22 μm were prepared by equal channel angular pressing (ECAP) and annealing. The deformation structure of UFG AZ31 alloy resulting from uniaxial compression was studied by optical and electron microscopy. The deformation was noted to proceed with the development of shear bands (SBs), which has not been reported in an UFG hcp metal. Characterization of these SBs was performed, and comparison with the SBs formed in UFG bcc and fcc metals was given. \( \{ 10\bar{1}2\} \) tension twins inside SBs were found in all specimens compressed, irrespective of the grain size. Discussion on the limiting grain size of twinning in the UFG AZ31 alloy is also given.