Site Preference and Diffusion in Ni3Al Alloyed with Ir, Ta or Re at 1200°C
2010
Diffusion in L12-Ni3Al with ternary alloying additions of Ir, Ta and Re was investigated at 1200°C using solid-to-solid diffusion couples, and examined with respect to site preference in ordered intermetallic compound. In addition to determination of average ternary interdiffusion coefficients [1-3], average effective interdiffusion coefficients were determined directly from the experimental concentration profiles. Ni has the largest magnitude of average effective interdiffusion coefficient, followed by Al, Ir, Re and Ta. The average effective interdiffusion coefficients for Ir, Re and Ta are much smaller than those for Ni and Al. Tracer diffusion coefficients determined by extrapolation technique, and available literature also followed the same trend. The relative tendency of Ni, Al, Ir, Re and Ta to occupy the -Ni and -Al sites are correlated to these diffusion coefficients, with due consideration for diffusion mechanisms and coordination of atoms.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
10
References
3
Citations
NaN
KQI