Electrochemical Studies on CaP Electrodeposition on Three Dimensional Surfaces of Selective Laser Melted Titanium Scaffold
2019
In this work, calcium phosphate (CaP) coating was electrodeposited on the three dimensional surface of SLM-Ti scaffolds. The in situ measurement showed that the potential variation within 5 mm thickness porous selective laser melting (SLM)-Ti samples was about 80 mV as a result of the low conductivity of CaP coatings. SEM observation results revealed that the coating morphology depended on the distance between the surface position of porous SLM-Ti electrode and the auxiliary electrode. Based on the compared electrochemical experiments, it was found that the top and the bottom surfaces of SLM-Ti scaffolds exhibited continuous nucleation and instantaneous nucleation behavior respectively. The Electrochemical impedance spectroscopy (EIS) results also revealed that the electrodeposition processes at different depth of SLM-Ti scaffolds were not synchronized. These differences were ultimately caused by the non-uniform distribution of the potential and the current inside porous SLM-Ti electrodes. The present work provides a basic research method for studying the mechanism of the electrochemical process on three dimensional surfaces of SLM-Ti scaffolds.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
29
References
4
Citations
NaN
KQI