Structure, acidity and redox properties of MCM-22 ferrisilicate

Abstract Aluminum-free MCM-22 type ferrisilicate, [Fe]MCM-22 (Si/Fe = 19.2) and, for comparison, MCM-22 aluminosilicate, [Al]MCM-22 (Si/Al = 13.1), were synthesized. The materials and their precursors were characterized by X-ray diffractometry (XRD), thermogravimetry (TG), transmission and diffuse reflectance Fourier-transform infrared spectroscopy (FT-IR and DRIFTS), temperature-programmed ammonia evolution (TPAE), in situ Mossbauer spectroscopy and temperature-programmed reduction with hydrogen (H 2 -TPR). The presence of Fe 3+ T atoms (Fe FW ) were indicated by the appearance of a ν OH IR-band at 3634 cm −1 . The red shift of the ν OH band, induced by the H-bonding of bridged hydroxyls and N 2 , was smaller for the [Fe]MCM-22 (64 cm −1 ) than for the [Al]MCM-22 (86 cm −1 ). The smaller shift evidences sites of weaker intrinsic acid strength. The rate and temperature of the TG-release of hexamethyleneimine template showed relation with the acidity of the sample. The amount of Fe 3+ species, present in highly distorted tetrahedral coordination state, was in good correspondence with the concentration of the Bronsted acid sites. After reduction with H 2 or CO, Fe 2+ appeared in a novel coordination state. Results suggest that these Fe 2+ species are bound to the framework via oxygen atoms. Reducibility of the framework iron is related to the high concentration of hydroxyl nests generated in both the wide (12-MR) and the narrow (10-MR) channels of [Fe]MCM-22 during the synthesis and/or template removal.