Role of hard martensite phase prior to cold-rolling on microstructure evolution after annealing in ferritic stainless steel
2016
Abstract To improve the surface quality of 16mass%Cr ferritic stainless steel sheets processed by cold-rolling and subsequent annealing, the role of the hard martensite phase, in particular, the hardness ratio k between martensite and ferrite prior to cold-rolling on microstructure evolution was investigated by varying the k value through tempering specimens at different temperatures after intercritical annealing. In the specimen with the high ratio k (k>2.0), the heterogeneous deformation in ferrite around the hard martensite becomes prominent and the areas with the high KAM value are locally limited with less development of cold-rolling texture. The specimen with the small ratio k (k 2.0 becomes fine, because the presence of hard martensite provides the nucleation site of recrystallization leading to fragmenting the elongated {100} colony structure, and the orientation is randomized. Consequently, the presence of the hard martensite phase prior to cold-rolling is effective for preventing the ridging of ferritic stainless steel sheets.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
18
References
6
Citations
NaN
KQI