Growth and lasing of single crystal YAG fibers with different Ho 3+ concentrations

Abstract A method to grow single crystal (SC) yttrium aluminum garnet (YAG) fibers with varied rare-earth ion dopant concentration has been proposed. Crystalline holmium aluminum garnet (HoAG), prepared via sol-gel process, was dip-coated on to previously grown SC YAG fibers. The HoAG coated SC YAG fiber preforms were re-grown to a smaller diameter using the laser heated pedestal growth (LHPG) technique. The final dopant concentration of the re-grown SC fiber was varied by changing the number of HoAG coatings on the preform. 120 μm diameter SC Ho:YAG fibers with four different dopant concentrations were grown. Lasing was demonstrated at 2.09 μm for these fibers. A maximum of 58.5% optical-to-optical slope efficiency was obtained.