Long chain branching and solution properties of low density polyethylene

The intrinsic viscosity, osmotic pressure and light scattering of solutions of fractionated samples of low density polyethylene (LDPE) were measured to study its long chain branching. The following relation was obtained between the two branching indices: gη is the ratio of the intrinsic viscosities of the branched and linear polymers with the same molecular weight, and gs is the corresponding ratio of the radii of gyration. The average number of long branches per molecule, nw, was calculated according to the theory of ZIMM and STOCKMAYER derived for random branching, and it was found that the dependence of nw on the molecular weight is expressed by with α = 0.85. This relation indicates that the long branching frequency or density decreases gradually with molecular weight for LDPE. Die Langkettenverzweigung von Polyathylen niedriger Dichte (LDPE) wurde experimentell untersucht. Nach der Bestimmung von Viskositatszahl, osmotischem Druck und Lichtstreuung der fraktionierter. Proben wurden folgende Beziehung zwischen zwei Indices der Langkettenverzweigung beobachtet: Hier bedeutet gη das Verhaltnis der Viskositaten von verzweigtem und linearem Polymeren mit gleichem Molekulargewicht und gs das Verhaltnis der Tragheitsradien der beiden entsprechenden Polymeren in der Losung. Nach der ZIMM-STOCKMAYER-Theorie, die an einem statistisch verzweigten Polymeren abgeleitet wurde, wurde die Anzahl der Langkettenverzweigungen pro Molekul, nw, berechnet; es wurde gefunden, das die Abhangigkeit von nw vom Molekulargewicht durch folgende Formel ausgedruckt werden kann: mit α = 0.85. Das bedeutet, das die Verzweigungshaufigkeit, d. h. die Verzweigungszehl pro Langeneinheit der Kette, langsam mit zunehmendem Molekulargewicht abnimmt.