Generation of microcellular poly(methyl methacrylate) by compressed gases

Abstract Generation of microcellular poly(methy1 methacrylate) (PMMA) was studied in CO2 and N2O at pressures from 2 to 15MPa at three temperatures, 293.2K, 308.2K, and 323.2 K. The average diameter d and average number density N of voids generated by a rapid expansion of compressed gases in PMMA were measured by use of an optical microscope. Effects of gases, temperature, and pressure on the d and N values were examined. Even at pressure below glass transition pressure of PMMA with both gases, voids of diameter being as small as those found at high pressure, 15MPa, were obtained at each temperature. However, the void density of PMMA at lower pressure by both gases was not so good as those obtained at high pressures.