Negative thermal quenching CsPbBr3 glass-ceramic based on intrinsic radiation and vacancy defect co-induced dual-emission
2021
Abstract Halide perovskite glass-ceramic has recently moved into the center of the attention of perovskite research due to their potential for temperature sensing. However, quantum dots glass-ceramic with excellent luminescence performance still needs to be combined with rare-earth (RE) ions to accurately measure temperature. In this work, a novel non-RE doped dual-emission (460 nm and 512 nm) CsPbBr3 quantum dots was obtained in telluride glass via the friction crystallization method, where 512 nm was derived from intrinsic luminescence of quantum dots, and 460 nm was originated from thermally induced bromine vacancy, which can be used for temperature sensing. Fluorescence intensity ratio results indicate that the relative sensitivity of dual-emission could reach 5.6 % K−1 at 323 K. The discovery of non-RE doped CsPbBr3 QDs glass-ceramic with negative thermal quenching uncovers a new optional sensing glass material that surpass traditional RE-doped QDs glass by their tunability and sensitivity.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
34
References
5
Citations
NaN
KQI