Electrical Resistivity of Chromium–Gold Alloys between 77 and 700 K

Electrical resistivity is measured as a function of temperature of binary chromium alloys containing 0.27, 0.54, and 0.60 at% gold. Gold decreases the Neel temperature linearly at a rate of 32 K/at% gold. Such a decrease is contrary to the predictions of conventional models for the antiferromagnetism in dilute chromium alloys, but can be explained if the excess nuclear charge on gold impurities is totally screened by the band electrons. Total screening also is consistent with the observed temperature variation of resistivity well above the transition temperature if, as seems reasonable, the scattering of electrons from gold impurities reduces the electronic density of states of the alloy at the Fermi energy. Der elektrische Widerstand von binaren Chromlegierungen mit 0,27; 0,54 und 0,60 At% Gold wird als Funktion der Temperatur gemessen. Gold verringert die Neeltemperatur linear mit einer Rate von 32 K/At% Gold. Ein derartiger Abfall befindet sich im Gegensatz zu den Vorhersagen der ublichen Modelle fur Antiferromagnetismus in verdunnten Chromlegierungen, last sich jedoch erklaren, wenn die uberschussige Kernladung an den Goldstorstellen vollstindig durch die Bandelektronen abgeschirmt wird. Vollige Abschirmung ist auch mit der beobachteten Temperaturanderung des Widerstands oberhalb der Ubergangstemperatur konsistent, wenn, was vernunftig scheint, die Streuung von Elektronen an Goldstorstellen die elektronische Zustandsdichte der Legierungen bei der Fermienergie reduziert.