The effect of boron nitride on electrical conductivity of nanocarbon-polymer composites

The electrical conductivity concentration and temperature dependences of polymer composite materials (CMs) with nanocarbon fillers [graphite nanoplatelets and multi-walled carbon nanotubes (MWCNTs)] were investigated. Epoxy resin modified with organosilicon compound was used as polymer matrix. The content of nanocarbon filler in varied from 1 to 10 wt%. To study of the synergetic properties the additional dispersed dielectric filler—boron nitride (BN) was added to given systems in content of 27 wt%. The electrical resistivity of CMs was investigated in the temperature range of 77–300 K. In the studied CMs the percolation transition at sufficient low filler content (0.01–0.022 vol. fr.) was observed. The values of critical index varied from 3.0 to 5.2. The electrical conductivity of investigated CMs was analyzed in the framework of proposed model that takes into consideration the morphology of filler particles. It was shown that the increase of electrical conductivity of GNP-polymer CM in the presence of BN is attributed to the decrease of contact resistance between filler particles, while for MWCNT-polymer CM is due to the increase of the number of conductive chains in this particular system.