Electrical Characteristics of TiW/ZnO Schottky contact with ALD and PLD

An electrical and analytical study was carried out to investigate TiW/ZnO Schottky contacts with 30 nm ZnO thin film layers deposited by pulsed laser deposition (PLD), plasma enhanced atomic layer deposition (PEALD), and thermal atomic layer deposition (TALD). Devices with ZnO layer deposited by TALD exhibit approximately linear behavior in their I-V measurements. However, both devices with ZnO layers deposited by PEALD and PLD behaved like Schottky rectifiers with barrier heights between TiW and ZnO of 0.51 eV and 0.45 eV respectively and ideality factors of 2.0 and 2.3 respectively. The PEALD deposited ZnO Schotty diodes demonstrated an on/off rectifying ratio of about 25 at ±1 V. The leakage current values of the PLD deposited ZnO Schottky diodes are significantly larger than those of PEALD, leading to a poor on/off rectifying ratio of ∼4. Due to the small thickness, a critical breakdown strength of 1.3 MV/cm was estimated for PEALD-ZnO thin films.