Novel Pickering Emulsifiers Based on pH-Responsive Poly(2-(diethylamino)ethyl methacrylate) Latexes

The emulsion copolymerization of 2-(diethylamino)ethyl methacrylate (DEA) with a divinylbenzene cross-linker in the presence of monomethoxy-capped poly(ethylene glycol) methacrylate (PEGMA) at 70 °C afforded near-monodisperse, sterically stabilized PEGMA-PDEA latexes at 10% solids. Dynamic light scattering studies indicated intensity-average diameters of 190 to 240 nm for these latexes at pH 9. A latex-to-microgel transition occurred on lowering the solution pH to below the latex pKa of 6.9. When dilute HCl/KOH was used to adjust the aqueous pH, a systematic reduction in the cationic microgel hydrodynamic diameter of 80 nm was observed over ten pH cycles as a result of the gradual buildup of background salt. However, no such size reduction was observed when using CO2/N2 gases to regulate the aqueous pH because this protocol does not generate background salt. Thus, the latter approach offers better reversibility, albeit at the cost of slower response times. PEGMA-PDEA microgel does not stabilize Pickering ...