Production and Characterization of Al-Si Coatings Fabricated by Mechanical Alloying Method on Inconel 625 Superalloy Substrates

Inconel superalloys are used substantially in high-temperature environments. However, these alloys suffer from corrosion and wear. Attempts to overcome these drawbacks involve coating the metal with different techniques and materials. In this study, a new method with increasing potential was utilized. Using the mechanical alloying process in a planetary ball mill vial, alloying and the Al-Si coatings were concurrently achieved on Inconel 625 substrates. Different process control agent (PCA) ratios, milling ball diameters, and milling times were used to improve coating properties. Macro and microstructure, morphology, microhardness, and roughness values of samples were evaluated and compared. Additionally, crystallographic and cross-sectional properties were investigated in order to optimize the processing conditions. The results indicated that increasing the diameter of the grinding ball enhanced the hardness and thickness of these coatings and increased the roughness values. Longer processing time also enhanced the thickness with mechanical values. However, under these conditions, coating homogeneity decreased, and incompatible regions were formed on the coatings. PCA content brought a refined grain structure, hence showed better mechanical properties. On the other hand, processing time should be increased to get a denser and thicker protective layer against the operational conditions.