Fabrication of La2Ti2O7 Crystals Using an Alkali-Metal Molybdate Flux Growth Method and Their Nitridability To Form LaTiO2N Crystals under a High-Temperature NH3 Atmosphere

Flux growth is a promising method that allows one to control over the crystalline phase, crystal shape, crystal size, and crystal surface through the selection of a suitable flux. In this work, lanthanum titanate (La2Ti2O7) crystals with different morphologies were grown using the Na2MoO4, K2MoO4, NaCl, and mixed NaCl + K2MoO4 (molar ratio = 3:7) fluxes, and their nitridability to form LaTiO2N crystals under a high-temperature NH3 atmosphere was also investigated. The effects of the solute concentration and cooling rate on the growth of the La2Ti2O7 crystals were also studied. The X-ray diffraction results revealed that the {100} plane was dominant in the La2Ti2O7 platelet crystals grown using the alkali-metal molybdate fluxes. When the solute concentration was increased from 1 to 20 mol %, the average size of the crystals decreased without considerable alteration of the overall crystal morphology. The La2Ti2O7 crystals with the preferred ⟨010⟩ and ⟨001⟩ growth directions along the b and c axes were grown...