Carbon nanotube growth for field-emission cathodes from graphite paste using Ar-ion bombardment

Multiwall carbon nanotubes (MW-CNT) have been synthesized from solid-phase graphite. The graphite is deposited as a thick-film paste and irradiated with a 1.2keV flood Ar-ion beam, transforming the graphite surface to a composite of MW-CNT embedded in the graphite matrix. Micro-Raman measurements have verified that the nanotubes are metallic in nature. The technique was used to make printed field-emission cathodes. Emission from these cathodes demonstrates Fowler–Nordheim tunneling characteristics. The irradiated film emits at an extraction field of 5.0V∕μm, which is less than one-sixth of the minimum extraction field of the nonirradiated graphite film, and exhibit lower noise and greater emission uniformity.