Optoelectronic properties of Cu1−xPtxFeO2 (0 ≤ x ≤ 0.05) delafossite for p-type transparent conducting oxide

Abstract The samples of Cu 1− x Pt x FeO 2 (0 ≤  x  ≤ 0.05) delafossite have been synthesized by solid-state reaction method to investigate their optical and electrical properties. The properties of electrical resistivity and Seebeck coefficient were measured in the high temperature ranging from 300 to 960 K, and the Hall effect and the optical properties were measured at room temperature. The obtained results of Seebeck showed the samples are p -type conductor. The optical properties at room temperature exhibited the samples are transparent visible light material with optical direct gap 3.45 eV. The low electrical resistivity, hole mobility and carrier density at room temperature displayed value ranging from 0.29 to 0.08 Ω cm, 1.8 to 8.6 cm 2 /V s and 1.56 × 10 18 to 4.04 × 10 19  cm −3 , respectively. The temperature range for transparent visible light is below 820 K because the direct energy gap contains value above 3.1 eV. Consequently, the Cu 1− x Pt x FeO 2 delafossite enhance performance for materials of p -type transparent conducting oxide (TCO) with low electrical resistivity.