Self-diffusion of silicon in molybdenum disilicide

The self-diffusion of silicon in single crystal MoSi2 was studied by means of a radiotracer technique using the short-lived radioisotope 31Si (half-life ), which was produced and implanted into the samples at the ion-guide isotope separator on-line device at the University of Jyvaskyla in Finland. Diffusion annealing and subsequent serial sectioning of the specimens were performed immediately after the radiotracer implantation. In the entire temperature region investigated (835–1124 K), the 31Si diffusivities in both principal directions of the tetragonal MoSi2 crystals obey Arrhenius laws, where the diffusion perpendicular to the tetragonal axis is faster than parallel to it. In previous studies the same features were observed for the 71Ge diffusivities in MoSi2, except that these are somewhat higher than those of 31Si. Furthermore, it is noteworthy that in MoSi2 the diffusivities of 31Si and 71Ge are orders of magnitude faster than the diffusivity of 99Mo. This large difference suggests that silicon dif...