Density Changes in Plutonium Observed from Accelerated Aging Using Pu-238 Enrichment

In support of Stockpile Stewardship activities, accelerated aging tests on a plutonium alloy enriched with 7.3 atomic percentage of {sup 238}Pu is underway using dilatometry at 35, 50, and 65 C and immersion density measurements of material stored at 50 C. Changes in density are expected from radiation damage in the lattice and helium in-growth. After twenty-five equivalent years of aging, the dilatometry data shows that the alloys at 35 C have expanded in volume by 0.11% to 0.12% and have started to exhibit a near linear expansion behavior primarily caused by the helium accumulation. The average He-to-vacancy ratio from tested specimens was determined to be around 2.3. The model for the lattice damage and helium in-growth accurately represents the volume swelling at 35 C. The density converted from the dilatometry corresponds well to the decreasing density trend of reference plutonium alloys as a function of time.