Torsional fatigue mechanisms of an A357-T6 cast aluminium alloy
2020
The mechanisms controlling the fatigue response of an A357-T6 cast aluminium alloy under cyclic torsional loading are investigated. Surface crack monitoring coupled with Electron BackScattering Diffraction (EBSD) analysis is used to study crack initiation. Determination of S-N curve combined with interrupted in situ fatigue testing using synchrotron tomography allows the study of the propagation behaviour. It is observed that fractographic morphologies depend on the stress level. At intermediate-low stress level (τmax < 100 MPa) the crystallography controls crack initiation and propagation periods. Cracks are usually nucleated in mode II from slip planes close to the specimen axis or perpendicular to it. Mode II crack growth dominates the early stages of crack propagation as mode III inward crack growth is rapidly decelerated. This behaviour leads to the formation of characteristic shallow cracks. Once the crack is long enough for the mode II driving force to be overtaken by mode III, propagation branches into ∼ 45∘ mode I.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
45
References
2
Citations
NaN
KQI