QD lasers: physics and applications

Quantum dot (QDs) heterostructures structurally represent tiny 3D insertions of a narrow bandgap material, coherently embedded in a wide-bandgap single-crystalline matrix. The QDs are produced by conventional epitaxial techniques applying self-organized growth and behave electronically as artificial atoms. Strain-induced attraction of QDs in different rows enables vertically-coupled structures for polarization, lifetime and wavelength control. Overgrowth with ternary or quaternary alloy materials allows controllable increase in the QD volume via the island-activated alloy phase separation. Repulsive forces during overgrowth of QDs by a matrix material enable selective capping of coherent QDs, keeping the defect regions uncapped for their subsequent selective evaporation. Low-threshold injection lasing is achieved up to 1350 nm wavelength at 300K using InAs-GaAs QDs. 8 mW VCSELs at 1.3 μm with doped DBRs are realized. Edge-emitters demonstrate 10 GHz bandwidth up to 70°C without current adjustment. VCSELs show ~4 GHz relaxation oscillation frequency. QD lasers demonstrate above 3000 h of CW operation at 1.5 W at 45°C heat sink temperature without degradation. The defect reduction technique (DRT) applied to thick layers enables realization of defect-free structures on top of dislocated templates. Using of DRT metamorphic buffer layers allowed 7W GaAs-based QD lasers at 1500 nm.