The determination of the residual strains and stresses in a tungsten inert gas welded sheet of IN718 superalloy using neutron diffraction

The residual stress state in a tungsten inert gas (TIG) welded sheet of IN718, a high-strength nickel-based superalloy, has been characterized using neutron diffraction. The measurements were performed using a time-of-flight diffractometer, which allowed lattice strains from the γ-γ′ {111} and γ-γ′ {311} composite peaks to be compared with the Reitveld-refined spectra. Residual stresses were estimated using plane-specific values of Young's modulus and Poisson's ratio for the {311} and {111} peaks, and the macroscopic material response for the Reitveld-refined data. These values were obtained from a theoretical analysis of existing data after Kroner.The weld considered was an autogenous TIG weld 180mm long placed centrally on to a 2mm × 100mm × 200mm solution heat-treated sheet of IN718. The strain was mapped over the central 140mm of the plate; within this region, the measured strains were almost constant along the length, with the peak bulk longitudinal strain of 1700 × 10-6 detected 4mm from the weld ce...