Effects of surface and sizing treatments on axial compressive strength of carbon fibres

Attempts have been made to estimate the fibre axial compressive strength of pitch-based graphitized fibres, and the effects of surface- and size-treatment on compressive strength was investigated. The estimated compressive strength of fibres decreases with increasing temperature. This decrease in compressive strength may be accounted for by a decrease in the radial compression force owing to a decrease in the residual thermal stress and a decrease in Young's modulus of the resin matrix. There is a linear relationship between the estimated compressive strength and radial compression force in a temperature range from room temperature to 80 °C. The real compressive strength of the fibres, determined by extrapolating this straight line until the radial compression force is zero, increases with increasing shear yield strength at the fibre-matrix interphase. In order to obtain reinforcing fibres with a higher compressive strength, it will be necessary to surface- and size-treat the fibres.