Magnetostructural transitions and magnetocaloric effects in Ni50Mn35In14.25B0.75 ribbons

The structural, thermal, and magnetic behaviors, as well as the martensitic phase transformation and related magnetocaloric response of Ni50Mn35In14.25B0.75 annealed ribbons have been investigated using room-temperature X-ray diffraction (XRD), differential scanning calorimetry (DSC), and magnetization measurements. Ni50Mn35In14.25B0.75 annealed ribbons show a sharper change in magnetization at the martensitic transition, resulting in larger magnetic entropy changes in comparison to bulk Ni50Mn35In14.25B0.75. A drastic shift in the martensitic transformation temperature (TM) of 70 K to higher temperature was observed for the annealed ribbons relative to that of the bulk (TM = 240 K). The results obtained for magnetic, thermal, structural, and magnetocaloric properties of annealed ribbons have been compared to those of the corresponding bulk alloys.