Stabilization of Iron Oxide Nanoparticles in High Sodium and Calcium Brine at High Temperatures with Adsorbed Sulfonated Copolymers

A series of sulfonated random and block copolymers were adsorbed on the surface of ∼100 nm iron oxide (IO) nanoparticles (NPs) to provide colloidal stability in extremely concentrated brine composed of 8% wt NaCl + 2% wt CaCl2 (API brine; 1.4 M NaCl + 0.2 M CaCl2) at 90 °C. A combinatorial materials chemistry approach, which employed Ca2+-mediated adsorption of anionic acrylic acid-containing sulfonated polymers to preformed citrate-stabilized IO nanoclusters, enabled the investigation of a large number of polymer coatings. Initially a series of poly(2-methyl-2-acrylamidopropanesulfonate-co-acrylic acid) (poly(AMPS-co-AA)) (1:8 to 1:1 mol:mol), poly(styrenesulfonate-block-acrylic acid) (2.4:1 mol:mol), and poly(styrenesulfonate-alt-maleic acid) (3:1 mol:mol) copolymers were screened for solubility in API brine at 90 °C. The ratio of AMPS to AA groups was varied to balance the requirement of colloid dispersibility at high salinity (provided by AMPS) against the need for anchoring of the polymers to the iro...