Kinetics of free radical polymerization of N,N‐dimethyl‐N,N‐diallyl‐ammonium‐chloride in concentrated aqueous solution

Radical polymerization kinetic of N,N-dimethyl-N,N-diallylammoniumchloride was investigated in concentrated aqueous solutions ([MI] = 2 to 5 mol/l, 60°C ) a t low conversions. It was shown that under choosen conditions there was no degradation transfer to monomer reactions in this case and polymerization had square order on persulfate ammonium concentration ([PSA] = 5 · 104 to 5 · 103 mol/l). The viscosity of the initial monomer solution influences greatly the bimolecular termination constant, which leads to sharp and nonlinear increase of the rate of polymerization with increasing monomer concentration. Untersuchungen zur Kinetik der radikalischen Polymerisation von N,N-Dimethyl-N,N-diallylamnloniumchlorid ([MI] = 2 bis 5 mol/l, T = 6O°C) bei niedrigen Umsatzen ergaben eine Reaktionsordnung bezuglich der Initiator-konzentration von 0,5 (Ammoniumpersulfat 5 · 104 bis 5 · 103, mol/l) sowie das Fehlen einer degradativen Ketten-ubertragung zum Monomer. Nachgewiesen wurde ferner ein wesentlicher Einflus der Viskositat der Ausgangsmonomerlosungen auf die Geschwindigkeitskonstante des bimolekularen Ketteirabbruchs sowie ein starker nichtlinearer Airstieg der Polymerisationsgeschwindigkeit mit Erhohung der Monomerkonzentration.