Studies on β‐picolinium‐p‐chlorophenacylide initiated copolymerization of methyl methacrylate with styrene

The alternating copolymerization of methyl methacrylate (MMA) with styrene (S) using β-picolinium-p-chlorophenacylide (β-PCPY) as radical initiator at 55, 60, and 65°C for 3 h has been kinetically investigated. The copolymerization rate (Rp) is proportional to the square root of [β-PCPY] and indicates bimolecular termination. The average degree of polymerization decreases as [β-PCPY] increases. The values of kp2/kt and energy of activation have been evaluated as 1.43 · 10-3 l mol-1 s-1 and 87 kJ mol-1, respectively. The NMR spectroscopy has been used to determine the structure, composition, and stereochemistry of copolymers. Die alternierende Copolymerisation von Methylmethacrylat mit Styrol unter Verwendung von β-Picolinum-P-chlorphenacylid als Radikalinitiator bei 55, 60 und 65°C und einer Reaktionszeit von 3 h wurde kinetisch untersucht. Die Copolymerisationsgeschwindigkeit (Rp) ist proportional der Quadratwurzel der Initiatorkonzentration und weist auf einen bimolekularen Abbruch hin. Der durchschnittliche Polymerisationsgrad nimmt mit zunehmender Initiatorkonzentration ab. Die ermittelten Werte fur kp2/kt und fur die Aktivierungsenergie betragen 1,43 · 10-3 l mol-1 s-1 bzw. 87 kJ mol-1. Die NMR Spektroskopie wurde zur Bestimmung der Struktur, Zusammensetzung und Stereochemie der Copolymeren verwendet.