Organosilicon coating and preparation method thereof

The invention belongs to the field of organosilicon, and particularly relates to an organosilicon coating and a preparation method thereof. The organosilicon coating is characterized in that the organosilicon coating comprises 90 to 120 parts of Alpha, Omega-dihydroxy polydimethylpolysiloxane, 10 to 30 parts of MQ resin, 10 to 30 parts of white carbon black, 0.3 to 1 part of vulcanization accelerators, 2 to 3 parts of methyl-tri-(butanone-oxime) silane, 2 to 3 parts of vinyl tributanoximo silane, 1 to 3 parts of propylamino triethoxy silane, 1 to 2 parts of 3-glycidyl ether oxypropyl trimethoxysilane and 70 to 90 parts of solvent. The preparation method comprises the steps of raw material selection, raw material weighing, rubber compound drying, rubber compound preparation, and the like. The organosilicon elastic coating disclosed by the invention has low viscosity and high fluidity, can be rapidly self-leveled and filled after being coated, has a high curing speed at room temperature, needs short surface drying time and curing time, has excellent electric insulation performance, high strength, low hardness, high elasticity and good toughness after being cured, has self-repairing performance and an elongation percentage reaching 200 to 500 percent, has good bonding performance, has shear strength of 2 to 5MPa over aluminum, has little odor, cannot corrode a matrix, adopts solvent oil as the solvent, can effectively insulate and protect the surfaces of printed circuit boards (PCB) and electronic devices, and can also used as other elastic coatings needing insulation performance and anticorrosion performance.