On the relief of transformation strains in γ‐phase Cr5Al8

The microstructure of the low-temperature rhombohedral phase (γ2) in the AlCr system resulting from transformation of the high-temperature γ1-phase during quenching is studied by transmission electron microscopy. It is found that the γ2-crystal is fragmented into domains separated by two types of twin interfaces which are parallel to {001} and {110} planes, respectively. Since the individual domain is characterized by the direction of its trigonal axis, four orientation variants exist. It is shown that such regular fragmentation of the crystal nearly completely relieves the strains caused by the rhombohedral distortion of the original cubic lattice. Das Gefuge der rhomboedrischen Tieftemperaturmodifikation (γ2) in dem System AlCr wird elektronenmikroskopisch untersucht. Es wird gefunden, das der wahrend der Abschreckung der Hochtemperaturmodifikation (γ1) entstandene γ2-Kristall regelmasig in Domanen aufgeteilt ist. Diese Domanen sind durch zwei Typen der Zwillingsgrenzen parallel zur {001}- und {110}- Ebene getrennt. Die Domanen entstehen in vier Orientierungsvarianten, da die einzelne Domane durch die Richtung ihrer trigonalen Achse charakterisiert ist. Die rhomboedrische Verzerrung des ursprunglich kubischen Gitters verursacht im Gitter Umwandlungsspannungen. Es wird gezeigt, das diese durch die beobachtete regulare Aufteilung des Kristalls fast vollstandig eliminiert sind.