Solid state amorphization of Mg-Zn-Ca system via mechanical alloying and characterization

Abstract Magnesium based bulk metallic glasses have attracted significant attention of researchers due to better mechanical and corrosion properties when compared to their crystalline counterparts especially for biomedical applications. Scaling up the part size and production volumes of such materials through liquid metallurgy route is challenging. In this work amorphous Ca 5 Mg 60+ x Zn 35− x ( X  = 0, 3 and 7) alloys have been successfully synthesized through solid state amorphization using a high energy planetary ball mill. X-ray diffraction was used to identify the crystalline phases of the powder during reaction. Evolution of amorphous phase was analysed using a parameter involving the ratio of integral area of peaks to the integral area of background ( I PB ) obtained from XRD patterns. Results showed reaction time increases with decreasing Zn content in Ca 5 Mg 60+ x Zn 35− x ( X  = 0, 3 and 7) alloy to obtain maximum amorphous structure with a small amount of residual crystalline phase. Prolonged milling of these powders, to eliminate residual crystalline phases, resulted in the nucleation of Mg 102.08 Zn 39.6 phase. The composition dependent characteristic temperatures and thermal stabilities were studied using differential scanning calorimetry.