High-Pressure Synthesis and Magnetism of the 4H-BaMnO3 Single Crystal and Its 6H-Type Polymorph.

A 4H-type BaMnO3 single crystal was prepared by combining the floating zone method with high-pressure treatment at 5 GPa and 1023 K. The crystal crystallizes to a hexagonal structure with space group P63/mmc and lattice parameters a = 5.63723(5) A and c = 9.22355(8) A. In this structure, face-sharing MnO6 octahedral dimers connect with each other by corner O atoms along the c-axis direction, forming an -A-B-A-C-type 4H arrangement. A long-range antiferromagnetic (AFM) phase transition is found to occur at TN ≈ 263 K. When the synthesis pressure increases to 20 GPa, a new polymorphic phase is obtained. This higher-pressure phase still possesses the hexagonal P63/mmc symmetry, but the lattice parameters change to be a = 5.61349(2) A and c = 13.66690(9) A with a unit cell volume reduction of 2.05%. In this new phase, the c-axis MnO6 dimers are separated by MnO6 octahedral layers in the ab plane, forming an -A-B-C-A-C-B-type 6H structure. The 6H phase exhibits two long-range AFM orderings at TN1 ≈ 220 K and TN2 ≈ 25 K, respectively. The different magnetic properties are discussed on the basis of the detailed structural constitutions of 4H- and 6H-BaMnO3.