Fast degradable poly(L-lactide-co-ε-caprolactone) microspheres for tissue engineering: Synthesis, characterization, and degradation behavior

Polymeric scaffolds play a crucial role in engineering process of new tissues and effect the cell growth and viability. PLCL copolymers are found to be very useful during cell growth due to their elastic behavior and mechanical strength. Thus, low molecular weight PLCL copolymers of various ratios viz. PLCL(90/10), PLCL(75/25), PLCL(50/50) and PCL were synthesized by ring opening polymerization using stannous octoate as a catalyst. Synthesized polymers were characterized by GPC, 1H-NMR, FTIR and XRD. The thermal properties of the copolymers were studied using TGA and DSC. Microspheres of about 100 μm diameter were prepared for different copolymers and their in vitro degradation behaviors were studied up to 108 days. It was observed that degradation of PLA content in polymer backbone occurs faster than PCL component which is also indicated by corresponding change in ratios of PLA/PCL, as determined by 1H-NMR. SEM images of microspheres depicted the surface morphology during degradation and suggested the faster degradation for PLCL (50:50). Copolymers of different thermal, mechanical properties and different degradation behaviors can be prepared by adjusting the composition of copolymers. Various synthesized polymers from this work have been tested in our laboratory as polymeric scaffold for soft tissue engineering. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2755–2764, 2007