니켈기 초내열합금 RENE 80 의 크리프시험중 결정입계 균열생성 및 전파

Two kinds of specimens with different microstructure were prepared by changing casting variables in vacuum investment casting. The effect of microstructural difference on the creep behavior, creep crack initiation and creep crack propagation was studied in Ni base superalloy RENE 80. The specimen having fine grained and uniformly distributed carbide exhibited superior creep properties to the large grained specimen tested at 760℃. However above 870℃, two kinds of specimens showed similar creep behavior. At higher temperature creep, crack initiation was principally caused by the reaction between the grain boundary exposed at the surface and the test atmosphere rather than the internal microstructural changes. The crack initiated at the surface propagated to the internal area and this kind of crack propagation leads to fracture of material.