Irradiation hardening and ductility loss of Eurofer97 steel variants after neutron irradiation to ITER-TBM relevant conditions

Abstract Ten Eurofer97 steel variants, produced by non-standard fabrication-processing routes and modified alloying chemistries, were studied by neutron irradiations in the high flux isotope reactor. The irradiations were performed to ITER-TBM relevant conditions of ∼255–350 °C, 2.94–3.24 dpa. We quantified the irradiation-induced degradation of the steels using mechanical property tests. All the steels suffered from irradiation hardening, where a significant increase in Vickers microhardness and yield stress (σYS) occurred, accompanied with severe loss of tensile elongation. The extent of hardening was material dependent. For Tirr = 300±30 °C, most steels showed σYS increase in the range of ∼30% to as high as ∼66%, except for a low temperature tempered steel with σYS increase below 15%. Despite large losses in elongation, most failures were ductile. Significant post-necking ductility was retained with reduction in area (RA) between 65–75%, but