Photocatalytic degradation of BTEX using W-doped TiO2 immobilized on fiberglass cloth under visible light
2012
Abstract W-doped TiO 2 were immobilized on fiberglass cloth (FGC). The catalyst possessed small crystallite sizes with a red-shift on an absorption edge. Good dispersion was observed over the immobilized catalyst. The photocatalytic degradation of gaseous BTEX was conducted in a flow reactor under day-light fluorescent. Parameters including gas flowrate, catalyst loading, initial concentration and relative humidity (%RH) were investigated. The prepared catalysts showed higher efficiency than that of TiO 2 approximately 18, 3, 3 and 2.5× for benzene, toluene, ethylbenzene and o -xylene, respectively. The condition to achieve 100% BTEX removal was found at 20 min/ml, catalyst loading 0.1 mg/cm 2 and 30% RH.