Application of Solution Plasma Surface Modification Technology to the Formation of Thin Hydroxyapatite Film on Titanium Implants

Hydroxyapatite (HA) coatings on titanium implants enhance rapid bone formation around the implant due to their osteoconductive property. The present study aimed to achieve a thin and uniform HA film coating on titanium implants by solution plasma treatment (SPT). Commercially pure titanium and porous titanium disks were employed. A pulse plasma generator was used on the disks for 30 min. Morphologic and crystallographic features of the deposited films were examined by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). To evaluate the wettability of the disks, water droplet (20 µL) surfaces were measured using a contact angle analyzer. The initial attachment of osteoblast-like cells (MC3T3E1) on the titanium substrates before and after solution plasma treatment was evaluated by counting the number of attached cells after incubation for 4 h. After immersion in the mineralizing solution for up to seven days, no crystals were observed on the polished-Ti surface. A more uniform and dense precipitation of round and grown crystals with diameters of approximately 1–5 µm was observed on Ti-SPT. XRD clearly showed that the precipitated crystals on titanium disks were HA. The contact angle of the polished-Ti increased with time (θ = 37°–51°). The surface of the Ti-SPT remained hydrophilic (θ ˂ 5°) after up to 30 days of aging. The number of attached cells on the Ti-SPT after aging for 30 days remained above 85% of that on the Ti-SPT without aging. SPT in a mineralizing solution can be used to acquire a homogenous precipitation of HA on porous-surfaced titanium implants.